DeFelsko Powder Comb

Powder Comb

Manufacturer: DeFelsko

Part #: PCX

Description: Check Powder thickness with Powder Comb before curing to help ensure correctly cured film thickness the first time through the line. Avoid stripping and re-coating which can cause problems with adhesion and coating integrity.

Features:

Works on a variety of part sizes, shapes and substrates such as metal, plastic, wood, glass, and more

Broad stand-offs on both sides of teeth help keep gage perpendicular to surface when measuring

Precision gage; manufactured to a tolerance ±5 microns or ±0.0002 inch

Protective leather pouch included with each gage

Versatility

Ideal for set-up and quality control

Works on a variety of part sizes, shapes and substrates such as metal, plastic, wood, glass, and more

Easy to carry; convenient shirt pocketsize

Available in microns (metric) or mils (imperial)

Quality

Broad stand-offs on both sides of teeth help keep gage perpendicular to surface when measuring

Rugged aluminum construction for long gage life and static control

Precision gage; manufactured to a tolerance ±5 microns or ±0.0002 inch

Protective leather pouch included with each gage

Simple Operation-

1. Push the Powder Comb perpendicularly into the dry powder so that the two stand-offs (end tabs) on both sides of the teeth rest firmly on the substrate.

2. Drag the Powder Comb along the surface of the coated part for at least 1 centimeter.

3. Remove the Powder Comb from the surface and examine the marks left in the powder.The powder thickness is between the highest numbered tooth which made a mark and has powder clinging to it, and the next highest tooth which left no mark and has no powder clinging to it.

Example: The 75 and 150 micron teeth both make lines and have powder clinging to them but the 225 mil tooth does not. The uncured powder thickness is determined to be between 150 and 225 microns. (see above image)

Note – Most powders cure to approximately 50% of their dry thickness. Marks left by the gage may affect the characteristics of the cured film.