Permabond ES562 Self-Leveling Single-Part Epoxy, White, 200ml Bottle

Physical Properties of Uncured Adhesive

Chemical composition: Epoxy Resin

Appearance: White

Viscosity @ 25°C: 15,000 – 30,000 mPa.s (cP)

Specific gravity: 1.2

Typical Curing Properties

Flow at high-temperature: Free flow

Maximum gap fill: 0.25mm (0.01″)

Cure speed (oven) *

130° C (266°F): 60 minutes

150°C (300°F): 45 minutes

160°C (320°F): 20 minutes

Cure speed (induction): <3>

*Actual cure times will depend on the time it takes for the adhesive to reach this temperature – for example, large assemblies or a crowded oven will require longer to reach full cure. Alternative, quicker methods of curing include induction, hotplates, infrared lamps, and hot-air guns.

Physical Properties of Cured Adhesive

Shear strength* (ISO4587):

Steel 20 – 35 MPa (3000 – 5000 psi)

Aluminium 14 – 27 MPa (2000 – 4000 psi)

Zinc 14 – 27 MPa (2000 – 4000 psi)

Tensile strength (DIN53504): 40 N/mm² (5800 psi)

Hardness (ISO868): 80-85 Shore D

E-modulus: 2.1 GPa

Elongation at break (DIN53504): <3>

Coefficient of thermal expansion:

50 x 10^-6mm/mm/°C (below Tg)

165 x 10^-6mm/mm/°C (above Tg)

Thermal conductivity: 0.25 W/(m.K)

Glass transition temperature (Tg – DSC): 115°C (240°F)

Water absorption (ISO62): <0>

*Strength results will vary depending on the level of surface preparation and gap.

Product Overview

More Information

SKU	I167272
Part No.	ES05620200B0101
Brand	Permabond
Type	Single-Part Epoxy
Volume	320ml