Permabond ET536 Toughened Two-Part Epoxy, White/Black, 50ml Cartridge

Physical Properties of Uncured Adhesive

	ET536A	ET536B
Chemical Composition	Epoxy Resin	Polyamine Hardener
Appearance	White	Black
Viscosity @25°C	20rpm: 75,000 mPa.s (cP) 2rpm: 225,000 mPa.s (cP)	20rpm: 150,000 mPa.s (cP) 2rpm: 300,000 mPa.s (cP)
Specific Gravity	1.1	1.2

Typical Curing Properties

Mix ratio by volume: 1:1

Maximum gap fill: 5mm (0.2″)

Usable / pot life @23°C: 50-80 mins

Handling time @23°C: 90-120 mins

Working strength @23°C:: 24 hours

Full cure @23°C: 72 hours

Typical Performance of Cured Adhesive

Shear strength* (ISO4587)

Mild steel: 22-32 N/mm² (3190-4640psi)

Aluminium: 22-26 N/mm² (3190-3770psi)

Stainless Steel: 26-30 N/mm² (3770-4350psi)

Carbon Fibre: 18-22 N/mm² (2610-3190psi)

FRP Glass/Polyester: 6-8 N/mm² (870-1160psi)

FRP Glass/Epoxy: 18-22 N/mm² (2610-3190psi)

Polycarbonate: 3-5 N/mm² (435-725psi)

PA6 30% filled: 4-6 N/mm² (580-870psi)

Peel strength (aluminum) (ISO111339): 70-90 N/25mm (16-21 PIW)

Hardness (ISO868): 65-75 Shore D

Elongation at break (ISO37): 4-8%

Glass transition temperature Tg: 45-55°C (113-131°F)

Dielectric Strength: 15-25 kV/mm

Thermal conductivity: 0.4 W/(m.K)

*Strength results will vary depending on the level of surface preparation and gap.